Capatect AmphiSilan Fassadenputz FREE

Ready-to-use silicone resin textured render without biocidal film protection according to DIN EN 15824
LV Texte

Field of Application

Ready-to-use, structurable silicone resin render for mineral and organic wall and ceiling surfaces outdoors without biocidal film protection. Can be used in connection with the Capatect facade systems.

Material Properties

  • Without biocidal film protection
  • Highly permeable to water vapor
  • Water repellent
  • Smooth processing
  • Can be diluted with water
  • Graduated, lightfast pigment-filler-granulate combination

Packaging/Package Size

25 kg bucket



Can be tinted by manufacturer. Suitable for machine tinting with dosing systems from ColorExpress.
Further custom colors with lightness value > 20 on request. If, for design reasons, colors with lightness value < 20 are required, these can be achieved in some cases with a double coat of Muresko CoolProtect paint.

Tinting of small quantities is possible by adding CaparolColor Vollton- und Abtönfarben (formerly Alpinacolor) or Amphibolin Vollton- und Abtönfarben. Do not add more than 2 % colour, otherwise the consistency will be too thin.

Gloss Level



Cool, dry and frost-free, avoid large temperature fluctuations. Protect from direct sunlight. Shelf life min. 12 months in original sealed packaging.


Approx. 1.8 g/cm³

Diffusion-equivalent air layer thickness sdH2O

< 0.14 m as per DIN ISO 7783
class V1 (high) as per DIN EN 15824

Fire behaviour

A2-s1, d0 as per DIN EN 13501-1 (non-combustible)



Vehicle / Binding agent

Silicone resin emulsion, acrylic resin dispersion

Water permeability (w-value)

≤ 0.1 kg/(m2·h0,5) as per DIN EN 1062-3
class W3 (low) as per DIN EN 15824

Product No.

Product-No.ProductStructureGrain size
Approx. consumption
626 FREECapatect AmphiSilan FassadenputzK20, scraped structure2.02.7
626 FREECapatect AmphiSilan FassadenputzK30, scraped structure3.03.6

The consumption figures are guide values without loss of bulk or shrinkage. Building-dependent or processing-related deviations must be taken into account.

Substrate Preparation

The substrate must be even, clean, dry, solid, sound/ stable and free from all substances that may
prevent good adhesion. In Germany follow VOB, part C, DIN 18 363, section 3.

Non-stable paint, emulsion paint or synthetic resin plaster coatings, as well as non-stable mineral coatings must be completely removed. Clean firmly adhering coatings dry or wet.

Clean mold, moss or algae-infested surfaces with pressurized water jets, observing the legal regulations. Wash thoroughly with Capatox and let the surfaces dry well. Clean surfaces soiled by industrial fumes or soot by means of pressurized water jets with the addition of suitable cleaning agents and in compliance with legal regulations.

Method of Application

Apply the render with a stainless steel trowel or suitable spraying equipment homogeneously
to surface sections. Rub off immediately to the grain size and take off excessive slurry. Immediately afterwards rub evenly in a circular motion with a plastic trowel or with a PU board. The surface roughness is influenced by the chosen tool, hence always the same type of texturing tool should be used.

For spray application the nozzle size depends on the grain size (nozzle size = 4 x grain size).
Working pressure: 0.3 to 0.4 MPa (3 to 4 bar). Apply thoroughly an homogeneous layer during spray
application. Avoid visible overlapping that may be caused by storeys of scaffolding.

Always the same craftsmen should finish seamless surfaces to achieve an even texture. To avoid
lapping on large-area surfaces, care should be taken to have a sufficient number of craftsmen on the
job and to apply the material wet-on-wet without interruption.

Granules and filler are natural products and therefore may occasionally cause slight colour variation in
the finished coating. Only use products of the same batch or, if materials from different batches must
be applied, mix the entire quantity needed in advance.

Capatect AmphiSilan Fassadenputz is not suitable for horizontal surfaces exposed to water.

Surface Coating System

The key coat Putzgrund 610 has to be tinted in matching colour shade before applying the tinted
finishing coat. Allow thorough drying of key/ intermediate coats before further application.

Capatect ETICS:
New mineral base coats (reinforcement layer): Prime with Putzgrund 610. New cement-free base
coats: No key coat required. Weathered base coats (e.g. after winter break): Prime with Putzgrund

Plasters of mortar groups PII u. PIII:
New plasters can be coated after a sufficient waiting period, usually after 2 weeks at approx. 20°C
and 65% rel. humidity. In less favorable weather conditions, e.g. influenced by wind or rain,
significantly longer waiting times must be observed. An additional key coat with CapaGrund Universal
reduces the risk of lime efflorescence, so that the finishing coat can be applied after just 7 days.
Intermediate coat with PutzGrund 610.

Old plasters:
Renewed plaster areas must be well set and dried out. Prime coarse, porous, absorbent, slightly
sanding plasters with OptiSilan TiefGrund. Intermediate coat with PutzGrund 610. Use
DupaPutzfestiger for heavily sanding, powdery plasters. Intermediate coat with PutzGrund 610.

Clean dirty or powdery concrete surfaces mechanically or with high pressure water jets in compliance
with the legal regulations. Use OptiSilan TiefGrund on coarsely porous, light sanding or absorbent
surfaces. On powdery surfaces, use Dupa-Putzfestiger. Intermediate coat with PutzGrund 610.

Load-bearing, matt emulsion paint coatings:
Coat matt, slightly absorbent coatings directly. Clean soiled, chalking old paint coatings with high
pressure water jets, observing the legal regulations. For other types of cleaning (washing, brushing off, hosing down), prime with Dupa-Putzfestiger. Intermediate coat with PutzGrund 610.

Application Conditions

During processing and in the drying phase, the ambient air and substrate temperatures must not drop below +5°C and be above +30°C. Do not use in direct sunlight, wind, fog or high humidity. With strong air movement on the surface at the time of execution and drying, there is a risk of shrinkage cracks and pore formation in the finishing coat.

Drying/Drying Time

At 20°C and 65% RH: surface-dry after approx. 24 hours. Cured, recoatable and ready for stress
after 2 to 3 days.
The render cures physically by evaporation of water. Drying time is extended by low temperature and
high RH.
Cover the scaffoldings with tarpaulins to protect the surface of the finishing coat from rain during the drying phase if necessary.
If necessary, the finished surface of the finishing coat must be protected until it is sufficiently weatherproof.

Tool Cleaning

Clean with water immediately after use.

Material Preparation

Stir the material thoroughly with a low-speed stainless steel agitator. If necessary adjust to working consistency with tap water (max. 1 % if manually applied and max. 2 % for spray application).

Special Risks (Hazard Note) / Safety Advice (Status as at Date of Publication)

May cause an allergic skin reaction. If medical advice is needed, have product container or label at hand. Keep out of reach of children. Do not get in eyes, on skin, or on clothing. Wear protective gloves/ eye protection. IF ON SKIN: Wash with plenty of soap and water. Take off contaminated clothing and wash it before reuse. Contains: 1,2-benzisothiazol-3(2H)-one, 2-methylisothiazol-3(2H)-one, reaction mass of 5-chloro-2-methyl-2H-isothiazol-3-one and 2-methyl-2H-isothiazol-3-one (3:1). Warning! Hazardous respirable droplets may be formed when sprayed. Do not breathe spray or mist.


Materials and all related packaging must be disposed of in a safe way in accordance with the full requirements of the local, regional, national and international authorities.





CE Labelling

The CE mark according to DIN EN 15824 is marked on the container and on the data sheet for the CE mark, which can be found on the Internet at

Customer Service Centre

Tel.: +49 6154 71-71710
Fax: +49 6154 71-71711

International Distribution: Please see